EN 10084: 2008 Steel Round Bar DIN 16MnCr5 SH (1.7131) 34 mm BG Hot Rolled Case Hardening Steel
EN 10084: 2008 Steel Round Bar DIN 16MnCr5 SH (1.7131) 34 mm BG Hot Rolled Case Hardening Steel
EN 10084: 2008 Steel Round Bar DIN 16MnCr5 SH (1.7131) 34 mm BG Hot Rolled Case Hardening Steel
EN 10084: 2008 Steel Round Bar DIN 16MnCr5 SH (1.7131) 34 mm BG Hot Rolled Case Hardening Steel
EN 10084: 2008 Steel Round Bar DIN 16MnCr5 SH (1.7131) 34 mm BG Hot Rolled Case Hardening Steel
EN 10084: 2008 Bar Rownd Dur DIN 16MnCr5 SH (1.7131) 34 mm BG Achos Rholio Poeth Caledu Dur
Fel cyflenwr a gwneuthurwr blaenllaw yn Tsieina, mae GNEE Steel yn darparu cynhyrchion aloi cost-effeithiol sy'n seiliedig ar nicel.
- Anfon e-bost:ss@gneesteel.com
- Ffôn:+8615824687445
EN 10084: 2008 Bar Rownd Dur DIN 16MnCr5 SH (1.7131) 34 mm BG Achos Rholio Poeth Caledu Dur
Disgrifiad
| OD: | 6-500mm | Arwyneb: | Du a Disglair |
|---|---|---|---|
| Hyd: | 3-12m | Cyflwr: | Triniaeth Gwres |
| Math: | Rholio Poeth | Gradd Dur: | Dur aloi |
| Aloi neu Beidio: | A yw aloi | Techneg: | Wedi'i rolio'n boeth, wedi'i ffugio, wedi'i dynnu'n oer |
| Siâp: | Rownd | Triniaeth arwyneb: | Du/Pilio/Caboli/Peiriannu |
| Diamedr: | 12mm-650mm | Amod Cyflwyno: | O fewn 15 diwrnod ar ôl derbyn blaendal |
| Dimensiynau: | 10mm ~ 800mm |
Bar Rownd Dur 16MnCr5 Bar aloi wedi'i rolio'n boeth EN10084 DIN 1.7131 Gwialen Aloi Arbennig
| Gradd : | 16MnCr5 | ||||
| Rhif: | 1.7131 | ||||
| Dosbarthiad: | Aloi dur arbennig | ||||
| Safon: |
|
||||
| Graddau cyfwerth: | Ewch yma |
Cyfansoddiad cemegol % o ddur 16MnCr5 (1.7131): EN 10084-2008
| Ni chaiff yr elfennau na ddyfynnir yn y tabl hwn eu hychwanegu'n fwriadol at y dur heb gytundeb y prynwr, ac eithrio at ddiben gorffen y gwres. Gellir cyflenwi dur gyda gwell peiriannu o ganlyniad i ychwanegu plwm neu gynnwys sylffwr uwch, yn dibynnu ar y broses weithgynhyrchu hyd at tua {{{{}}}}.1 % S, ar gais. Yn yr achos hwn, gellir cynyddu terfyn uchaf y cynnwys manganîs 0.15% |
| C | Os | Mn | P | S | Cr |
| 0.14 - 0.19 | uchafswm 0.4 | 1 - 1.3 | uchafswm 0.025 | uchafswm 0.035 | 0.8 - 1.1 |
Priodweddau mecanyddol dur 16MnCr5 (1.7131)
| Trwch enwol (mm): | i 16 |
| Rm - Cryfder tynnol (MPa) yn caledu a thymheru ar 200 | 1000 |
| Rm - Cryfder tynnol (MPa) (+A) | 550 |
| Rp0.2 0.2% cryfder prawf (MPa) (+A) | 420 |
| A - Min. elongation Lo=80 mm (%) (+A) | 21 |
| Z - Gostyngiad yn y trawstoriad ar dorri asgwrn (%) | 62-64 |
| Caledwch Brinell (HBW): (+A) | 207 |
| Caledwch Brinell (HBW): (+TH) | 156 - 207 |
| Caledwch Brinell (HBW): (+ FP) | 140 - 187 |
| Caledwch Brinell (HBW): (+ N) | 138 - 187 |
| Caledwch Rockwell B (HRB neu RB): (+A) | 84 |
| caledwch Vickers (HV): (+A) | 170 |
Priodweddau dur 16MnCr5 (1.7131)
| Weldability: Mae'n ddur aloi MnCr, sy'n hawdd ei beiriannu a'i weld yn boeth Caledadwyedd: Mae ganddo galedwch isel ac felly gall ddangos nodweddion craidd da hyd at drwch o tua 20 mm. |
Graddau dur cyfatebol 16MnCr5 (1.7131)
Rhybudd! Dim ond ar gyfer cyfeirio
| UE EN |
UDA - |
Almaen DIN,WNr |
Ffrainc AFNOR |
Lloegr BS |
Eidal UNI |
Sbaen UNE |
Tsieina GB |
Sweden SS |
Gwlad Pwyl PN |
Tsiecsia CSN |
Rwsia GOST |
Rhyng ISO |
|||||||||||||||
| 16MnCr5 |
|
|
|
|
|
|
|
|
|
|
|
|
Cyfleoedd NEWYDD i brynwyr!
Gofyniad prynu dur am ddim ar ôl 16MnCr5 (1.7131)
Priodweddau mecanyddol
| ReH | Cryfder cnwd lleiaf / Mindestwert der oberen Streckgrenze / Limite d elastigit minimale |
| Rm | Cryfder tynnol / Zugfestigkeit / Resistance a la traction |
| A | Lleiafswm elongation / Mindestwert der Bruchdehnung / Allongement minimal |
| J | Prawf effaith rhicyn / Kerbschlagbiegeversuch / Essai de flexion par choc |
Amodau triniaeth wres
|
|
|
Aloi dur arbennig |
Tagiau poblogaidd: ga 10084:2008 dur rownd bar din 16mncr5 sh (1.7131) 34 mm bg achos rholio poeth caledu dur, Tsieina en 10084:2008 dur rownd bar din 16mncr5 sh (1.7131) 34 mm bg poeth rholio achos caledu cyflenwyr dur