Beth yw Hastelloy C276 (Hastelloy C276)?
Hastelloy C276
1. Cyflwyniad i Hastelloy C276:
Hastelloy C276 alloy is mainly used to solve the intergranular corrosion of C grade, reducing the carbon and silicon in the alloy to very low levels, avoiding the intergranular continuous grain boundary precipitation phase in the welding heat affected zone, so that the alloy has no Intergranular corrosion. However, the thermal stability of the alloy is not good. Hastelloy C-276 alloy is one of the few materials that can be used in hot concentrated H2SO4 solutions. It is mainly resistant to wet chlorine, various oxidizing chlorides, chloride salt solutions, H2SO4 and oxidizing salts, and is resistant to both low and medium temperature HCl. Has very good corrosion resistance. Therefore, in the past thirty years, it has been widely used in harsh corrosive environments, such as chemical industry, petrochemical industry, flue gas desulfurization, pulp and paper making, environmental protection and other industrial fields.
2. hastelloy C276 ceisiadau a nodweddion:
Hastelloy C276 cais caeau: Mae hyn aloi yn bennaf defnyddio ar gyfer offer a cydrannau hynny handlen cryf cyfryngau, fel gwlyb clorin, clorid halwynau a amrywiol asidau organig a halogen nwyon. Alloy offer wedi llwyddiannus defnyddio yn ffosfforig asid, asid cynhyrchu a ffliw nwy desulfurization offer. os mae yn gofyniad i osgoi y risg o intergranular cyrydu ar ôl weldio, Shanghai Yuan Metelau Deunyddiau Co., Ltd. argymell hwn aloi. Y cyffredinol cyrydiad sefyllfa Hastelloy C{{1}% 7d aloi yw yr un yr un hynny C Y intergranular gwrthiant ar ôl weldio yw da, ond y posibilrwydd o intergranular cyrydu dal yn bodoli ar ôl weldio. Mae hyn aloi yn yn y weldio wladwriaeth neu solid ateb wladwriaeth.
3. Similar brands to Hastelloy C276:
| Newydd enw ar gyfer uchel tymheredd | uchel tymheredd hen enw | Newydd enw ar gyfer cyrydu gwrthwynebiad | Corrosion-resistant old name | GB |
| NS3304 | 00Cr16Ni60Mo16W4 | |||
| JIS | UNS,SAE | DWNDWR | DWNDWR | |
| Hastelloy C276 | N10276 | NiCrofer 5916hMoW | 2.4819 |
4. Cyfansoddiad cemegol o Hastelloy C276:
| C | Os | Mn | P | S | C |
| Less than or equal to 0.02 | Llai na neu cyfartal i 0.08 | Llai na neu hafal i 1.00 | Llai na neu hafal i 0.040 | Llai na neu cyfartal i 0.03 | 14.5~16.5 |
| Ni | Mo | N | Cu | Ab | Nbr |
| 基 | 15.00~17.0 | ~ | ~ | 4.0~7.0 | ~ |
| B | Ti: | Al | V | W | Ce |
| ~ | ~ | ~ | Llai na neu hafal i 0.35 | 3.0~4.5 | ~ |
5. eiddo eiddo o hastelloy C276% 3a
| dwysedd/cm�% B3 | magnetig | Thermal conductivity/w/(m.k)100~1092 degree | Gwrthedd gradd ) / (Ω.mm2/m) | Penodol gwres capasiti gradd ) /J/(kg.k) gradd | llinol ehangu cyfernod/ (10-6}/k)20~649 gradd |
| 8.885 | 9.4-28 | 1.3 | 427 | 14.1 |
6. Mechanical properties of Hastelloy C276
| Amrywiaeth | gwres triniaeth | tymheredd0/ gradd | tynnol cryfderRM\MPa | ElongationA/% | cyfradd o gostyngiad yn ardalZ/% |
| plate2.4 | Oer dadffurfiad0%Cold dadffurfiad 10% 25 | ystafell tymheredd | 806 | 67 | |
| ystafell tymheredd | 894 | 48 | |||
| plate2.4 | Oer anffurfiad 20% 25Oer dadffurfiad 40% 25 | ystafell tymheredd | 1021 | 26 | |
| ystafell tymheredd | 1336 | 9 |
7. Prosesu a weldio eiddo Hastelloy C276
Hastelloy C276 prosesu a weldio: prosesu poeth yn anodd anffurfio, y prosesu tymheredd yw {1}% 7d graddau, a y oer prosesu perfformiad yn da yn y ateb solet wladwriaeth. Y gwres triniaeth tymheredd is 1220 gradd. Shanghai Yuanding yn gyffredinol argymell dŵr oeri ar ôl solid ateb. Mae'r weldio perfformiad yn yn well na C.